Anode Cap seals and protects the critical connection between lead wire and anode.
Features
• The tight fitting, heat-shrinkable anode cap provides stress relief, moisture proofs and electrically insulated the end of the anode at the lead time exit point, it is the ideal. Solution to the problem of premature system failure due to loss of the wire to anode termination.
• Operating temperature: -45 ºC~105 ºC.
• Shrink temperature: Start at 100 ºC, and shrink totally at 130 ºC.
| Order ref. Number | B. D(mm) | C. D(mm) | B. L(mm) | C. L(mm) | B. W(mm) | ||
| Supplied | Recovered | Supplied | Recovered | ||||
| AC-2 | ≥ 58 | ≤ 48 | ≥ 12.5 | ≤ 6.5 | 76± 2 | 78± 2 | 2.4± 0.1 |
| AC-3B | ≥ 83 | ≤ 60 | ≥ 12.5 | ≤ 6.5 | 102± 2 | 78± 2 | 2.4± 0.1 |
| AC-4B | ≥ 120 | ≤ 87 | ≥ 13.5 | ≤ 6.5 | 102± 2 | 78± 2 | 2.3± 0.1 |
| AC-Φ 86 | ≥ 86 | ≤ 40 | ≥ 16.8 | ≤ 5.6 | 150± 2 | 78± 2 | 2.5± 0.1 |
| AC-Φ 112 | ≥ 112 | ≤ 55 | ≥ 16.8 | ≤ 5.6 | 150± 2 | 78± 2 | 2.5± 0.1 |
Technical Data
| Property | Test Method | Standard Value |
| Tensile strength | ASTM-D-2671 | ≥ 13MPa |
| Elongation at break | ASTM-D-2671 | ≥ 300% |
| Tensile strength after thermal aging | ASTM-D-2671(120 º C/168hrs) | ≥ 11MPa |
| Elongation at break after thermal aging | ASTM-D-2671(120 º C/168hrs) | ≥ 230% |
| Longitudinal shrinkage | UL 224 | ≤ 10% |
| Eccentricity | ASTM-D-2671 | < 30% |
| Water absorption | ISO 62 | ≤ 0.1% |
| Volume resistance | IEC 93 | ≥ 1× 10 14 Ω . cm |
| Dielectric strength | IEC243 | ≥ 20kV/mm |
| Resistance to stress cracking | ASTM-D-1693 (50 º C) | No cracking |
| Resistance to fungus and decay | ISO 846 | Pass |